膩子粉是建筑裝修中用于墻面找平的核心材料，其成分構成直接影響施工性能與墻面質量。從基礎骨架到功能添加劑，每一類成分都承擔著特定角色，共同構建起平整、耐久的墻面基底。

　　Putty powder is the core material used for wall leveling in building decoration, and its composition directly affects the construction performance and wall quality. From basic skeleton to functional additives, each type of component plays a specific role in building a smooth and durable wall base together.

　　無機膠凝材料：構建強度根基

　　Inorganic cementitious materials: building the foundation of strength

　　膩子粉的核心粘結成分以無機膠凝材料為主，其中熟石膏與白水泥占據主導地位。熟石膏通過與水反應生成二水石膏晶體，形成網絡狀骨架，賦予膩子初期強度與硬化性能，其2小時抗折強度可達3MPa以上。白水泥則憑借硅酸三鈣水化反應，提供長期耐久性，某品牌測試數據顯示，28天抗壓強度突破45MPa。在耐水型膩子中，灰鈣粉（氫氧化鈣）的加入使體系pH值提升至12以上，通過碳化反應生成碳酸鈣結晶，顯著提升耐水性能，經48小時浸水試驗后，粘結強度保持率仍超80%。

　　The core bonding components of putty powder are mainly inorganic cementitious materials, among which gypsum and white cement dominate. Mature gypsum reacts with water to form dihydrate gypsum crystals, forming a network like skeleton that endows putty with initial strength and hardening properties. Its 2-hour flexural strength can reach over 3MPa. White cement relies on the hydration reaction of tricalcium silicate to provide long-term durability. Test data from a certain brand shows that its compressive strength exceeds 45MPa after 28 days. In water-resistant putty, the addition of calcium hydroxide powder (calcium hydroxide) increases the pH value of the system to above 12, and generates calcium carbonate crystals through carbonation reaction, significantly improving water resistance. After 48 hours of immersion test, the bond strength retention rate still exceeds 80%.

　　礦物填料：塑造施工性能

　　Mineral fillers: shaping construction performance

　　填料體系以碳酸鈣類礦物為主，重質碳酸鈣（雙飛粉）因粒徑分布寬泛（5-50μm），成為調節膩子刮涂性的關鍵。其填充密度可達2.65g/cm3，有效減少收縮開裂。滑石粉的層狀結構賦予膩子優異的滑爽性，實驗室摩擦系數測試顯示，添加20%滑石粉可使膩子漿體摩擦系數降低至0.35，顯著提升施工手感。石英砂作為剛性填料，莫氏硬度達7級，在耐磨型膩子中占比可達30%，使表面硬度提升至鉛筆硬度2H級別。

　　The filling system is mainly composed of calcium carbonate minerals, and heavy calcium carbonate (double fly powder) becomes the key to adjusting the scraping properties of putty due to its wide particle size distribution (5-50 μ m). Can its filling density reach 2.65g/cm3 Effectively reduce shrinkage and cracking. The layered structure of talc powder endows putty with excellent smoothness. Laboratory friction coefficient tests have shown that adding 20% talc powder can reduce the friction coefficient of putty slurry to 0.35, significantly improving the construction feel. Quartz sand, as a rigid filler, has a Mohs hardness of 7 and accounts for up to 30% of wear-resistant putty, increasing the surface hardness to the pencil hardness level of 2H.

　　有機添加劑：實現功能升級

　　Organic additives: achieving functional upgrades

　　纖維素醚類添加劑是現代膩子的技術核心，羥丙基甲基纖維素（HPMC）通過氫鍵作用形成三維網絡，將保水率提升至98%以上，有效延長開放時間至2小時以上。可再分散乳膠粉的加入則引入聚合物膜結構，某測試表明，添加3%乳膠粉可使膩子層與水泥基材的拉伸粘結強度從0.4MPa提升至1.2MPa。針對特殊環境，淀粉醚提供觸變性能，使膩子在垂直面施工時抗流掛厚度達5mm，而聚丙烯短纖維（長度6mm）則將抗沖擊強度提升40%。

　　Cellulose ether additives are the technological core of modern putty. Hydroxypropyl methyl cellulose (HPMC) forms a three-dimensional network through hydrogen bonding, increasing the water retention rate to over 98% and effectively extending the opening time to over 2 hours. The addition of redispersible latex powder introduces a polymer film structure. A certain test shows that adding 3% latex powder can increase the tensile bond strength between the putty layer and the cement substrate from 0.4 MPa to 1.2 MPa. For special environments, starch ether provides thixotropic properties, making the putty resistant to sagging thickness up to 5mm when applied vertically, while polypropylene short fibers (length 6mm) increase impact strength by 40%.

　　功能性助劑：應對復雜工況

　　Functional additives: for complex working conditions

　　在潮濕地區，憎水劑（如有機硅氧烷）通過降低表面能，使膩子接觸角提升至110°，吸水率降低至5%以下。針對沿海鹽霧環境，防腐劑（如BIT類）以0.3%的添加量即可抑制95%的霉菌生長。冬季施工時，早強型促凝劑（如甲酸鈣）使-5℃環境下24小時強度發展達到常溫的70%，而緩凝劑（檸檬酸）則在高溫季將操作時間延長至3小時。

　　In humid areas, hydrophobic agents (such as organosiloxane) increase the contact angle of putty to 110 ° and reduce the water absorption rate to below 5% by reducing surface energy. For coastal salt spray environments, preservatives (such as BIT) can inhibit 95% of mold growth at a dosage of 0.3%. During winter construction, early strength accelerators (such as calcium formate) can achieve 70% of the strength development at room temperature within 24 hours in a -5 ℃ environment, while retarders (citric acid) can extend the operation time to 3 hours in high temperature seasons.

　　環保型替代方案

　　Environmentally friendly alternative solutions

　　隨著綠色建材發展，天然植物膠粉（如淀粉醚）正逐步替代部分化學添加劑，其生物降解率達98%。再生材料應用方面，建筑垃圾粉磨至200目后，可替代30%的碳酸鈣填料，既降低碳排放，又保持物理性能穩定。

　　With the development of green building materials, natural plant rubber powder (such as starch ether) is gradually replacing some chemical additives, with a biodegradation rate of 98%.  In terms of the application of recycled materials, after grinding construction waste to 200 mesh, it can replace 30% of calcium carbonate fillers, reducing carbon emissions while maintaining stable physical properties.

　　膩子粉的成分設計已從傳統配方演變為多組分協同體系，通過無機-有機復合、功能助劑集成，實現從單一找平向耐水、抗裂、環保等多元化性能跨越。施工者需根據基材特性、環境條件選擇適配產品，并嚴格遵循配比要求，方能充分發揮現代膩子的技術優勢。

　　The composition design of putty powder has evolved from traditional formulas to a multi-component collaborative system, achieving a diversified performance leap from single leveling to water resistance, crack resistance, environmental protection, etc. through inorganic organic composites and functional additives integration. Construction workers need to choose suitable products based on the characteristics of the substrate and environmental conditions, and strictly follow the proportioning requirements in order to fully utilize the technological advantages of modern putty.